Investigation of Through Porosity of Oxide Ceramic Coatings Formed by Plasma Electrolytic Oxidation
Ispitivanje poroznosti oksidnih keramičkih prevlaka nanetih plazma elektrolitičkom oksidacijom
Pregled/ Otvaranje
Autor
Kuznetsov, Yury
Chernyshov, Nikolay
Ključne reči
plasma electrolytic oxidationmicro arc discharges
current density
electrolyte
coating
through porosity
corrosive resistance
high temperature soldering
flux
plazma elektrolitièka oksidacija
mikro luèna pražnjenja
gustina struje
elektrolit
prevlaka
unutrašnja poroznost
otpor prema koroziji
visokotemperatursko lemljenje
fluks
Metadata
Prikaz svih podataka o dokumentuApstrakt
The article presents the results of investigation of through porosity of
oxide ceramic coatings obtained by plasma electrolytic oxidation (PEO) on the
aluminum parts surfaces, restored by soldering. The optimal modes and electrolyte
composition for plasma electrolytic treatment of the restored surfaces are recommended
to obtain oxide ceramic coatings with minimum through porosity and high coating and
corrosive resistance. U ovom radu su predstavljeni rezultati ispitivanja unutrašnje poroznosti
oksidno keramičkih prevlaka nanetih plazma elektrolitičkom oksidacijom (PEO) na
površine aluminijumskih delova, restauriranih lemljenjem. Za optimalne elektrolitičke
sastave za plazma elektrolitički tretman restauriranih površina preporučene su oksidne
keramičke prevlake sa minimalnom unutrašnjom poroznošću, visokom pokrivenošću i
otpornošću prema koroziji.